description:
SPECIFICATIONS
Type core |
Design |
Diameter, mm |
Protective environment |
Welding current |
The position of the seam |
---|---|---|---|---|---|
Carbonate-fluorenyl |
Tubular |
1,6; 2,0; 2,4 |
s/s |
=+ |
Downhand |
TYPICAL CHEMICAL COMPOSITION of DEPOSITED METAL, %
C |
Mn |
Si |
Cr |
Al |
Mo |
V |
S |
P |
---|---|---|---|---|---|---|---|---|
≤ 0,15 |
1,0 - 1,5 |
0,2 - 0,5 |
0,4 - 0,6 |
0,8 - 1,0 |
0,2 - 0,5 |
0,1 - 0,2 |
≤ 0,03 |
≤ 0,03 |
THE MECHANICAL PROPERTIES OF THE WELD METAL
σt, MPa |
σy, MPa |
δ,% |
An,J/sm2(+20oС) |
---|---|---|---|
600 - 750 |
≥ 540 |
≥ 18 |
≥ 80 |
MODES OF WELDING-CORED WIRE
Diameter,mm | Iсв,А | Uд,В | Extension, mm |
---|---|---|---|
1,6 |
150 - 280 |
20 - 28 |
25 - 35 |
2,0 |
200 - 350 |
22 - 30 | 25 - 35 |
2,4 |
250 - 450 |
24 - 32 |
25 - 35 |
A distinctive feature of the brands of wires АНПМ1, АНПМ2 and АНПМ3 is the possibility of their application for welding and surfacing consumable mouthpiece with forced formation of weld metal. This process is used for joining of steel parts with a thickness of 16...200 mm. The welding technology was developed by specialists of the Institute of Electric Welding. E.O.Paton of National Academy of Sciences of Ukraine.
The developed method of welding allows to obtain high-quality welds, including welding in installation and field conditions.